A complete experimental investigati

A complete experimental investigation in quasi-static compressive stress-strain
condition allowed us to understand mechanical behaviour of low and high
density carbon foams. In lateral confinement conditions the foam showed a wide
brittle crushing plateau which gives the same stress-strain curve shape of an
elastic – plastic behaving material. This part of the stress-strain curve shows a
very low strain hardening coefficient for the low density foam and a noticeable
one for the high density one. The modulus of elasticity was not modified by the
confinement. Passing from uniaxial stress to uniaxial strain, the failure evolution
changed without influencing the elastic behaviour. Therefore under confinement
multiaxial loading condition, these foams present energy absorption much higher
than in the case of simple compression, due to the extend crushing plateau.

Résultats (Français) 1:

Une enquête expérimentale complète dans le, car il était statique compression contrainte-déformation
état ​​nous a permis de comprendre le comportement mécanique de basses et hautes
mousses de densité de carbone. Dans des conditions de confinement latéral de la mousse a montré un large
plateau de broyage fragile qui donne la même contrainte-déformation courbe forme d'un
élastique - matériau de se comporter en plastique. Cette partie des courbes contrainte-déformation montrent un
coefficient d'écrouissage très faible pour la mousse de faible densité et un notable
un pour la haute densité une. Le module d'élasticité n'a pas été modifiée par le
confinement. Passant de contrainte uniaxiale à une contrainte uniaxiale, l'évolution de l'échec
changé sans influencer le comportement élastique. Donc sous confinement
Multiaxial conditions de chargement, ces mousses d'absorption d'énergie présente beaucoup plus élevé
que dans le cas de la compression simple, en raison de la Plateau étendre écrasement.